MICROSTRUCTURAL EVALUATION AND CYTOTOXICITY INVESTIGATIONS OF α-Al2O3 BONE REPLACEMENT MATERIALS

Objective: To evaluate the production of porous α-Al₂O₃ by slip casting method and to investigate the cytotoxicity by MTT and Agar diffusion tests as well as SEM microstructural evaluation.

Method: Ceramic process route includes slip casting for porous osteoconductive α-Al₂O₃ production. For examination of morphology, SEM was employed. To evaluate the cytotoxicity, MTT and Agar diffusion tests were conducted.

Results: The conducted tests have given very close results to positive control groups which mean that the product α-Al₂O₃ is a very good candidate for bone replacement and osteoconductivity.

Conclusions: The porous α-Al₂O₃ production was succeeded and the cytotoxicity tests have been approved that this material can be a good candidate for replacement.

Amaç: α-Al₂O₃’nın alçı kalıba döküm yöntemiyle gözenekli olarak üretilebilirliğinin değerlendirilmesi, MTT ve Agar difüzyon testleriyle sitotoksisitesinin ve SEM ile de mikroyapısal incelemesinin yapılması.

Yöntem: Gözenekli ve doku büyüyebilir α-Al₂O₃ üretimi için alçı kalıba döküm yöntemi kullanılmıştır. Morfolojik analiz için SEM kullanılmıştır. Sitotoksisite için MTT canlılık testi ve Agar difüzyon testi kullanılmıştır.

Bulgular: Yapılan testler, α-Al₂O₃’nın positif kontrol grubuna yakın canlılık değerleri verdiğini göstermiştir. Bu da aluminanın kemik ile yer değiştirebilir bir aday malzeme olabileceğini göstermektedir.

Sonuç: Gözenekli alumina üretimi başarılı olmuştur. Özellikle sitotoksisite testleri göstermiştir ki alumina kemikle yer değiştirebilir çok önemli ve uygun bir adaydır.