Objective: To evaluate the production of porous α-Al2O3 by slip casting method
and to investigate the cytotoxicity by MTT and Agar diffusion tests as well as
SEM microstructural evaluation.
Method: Ceramic
process route includes slip casting for porous osteoconductive α-Al2O3 production. For examination of morphology, SEM was employed. To evaluate
the cytotoxicity, MTT and Agar diffusion tests were conducted.
Results: The
conducted tests have given very close results to positive control groups which
mean that the product α-Al2O3 is a very good candidate
for bone replacement and osteoconductivity.
Conclusions: The porous α-Al2O3 production was succeeded and
the cytotoxicity tests have been approved that this material can be a good
candidate for replacement.
Anahtar Kelimeler
Kemikle yer değiştirebilir α-Al2O3 malzemelerin mikro yapısal değerlendirmesi ve sitotoksik incelemeleri
Öz
Amaç: α-Al2O3’nın alçı kalıba döküm
yöntemiyle gözenekli olarak üretilebilirliğinin değerlendirilmesi, MTT ve Agar
difüzyon testleriyle sitotoksisitesinin ve SEM ile de mikroyapısal
incelemesinin yapılması.
Yöntem: Gözenekli ve doku büyüyebilir α-Al2O3 üretimi
için alçı kalıba döküm yöntemi kullanılmıştır. Morfolojik analiz için SEM
kullanılmıştır. Sitotoksisite için MTT canlılık testi ve Agar difüzyon testi
kullanılmıştır.
Bulgular: Yapılan testler, α-Al2O3’nın
positif kontrol grubuna yakın canlılık değerleri verdiğini göstermiştir. Bu da
aluminanın kemik ile yer değiştirebilir bir aday malzeme olabileceğini
göstermektedir.
Sonuç: Gözenekli alumina üretimi başarılı olmuştur. Özellikle
sitotoksisite testleri göstermiştir ki alumina kemikle yer değiştirebilir çok
önemli ve uygun bir adaydır.
Anahtar Kelimeler
Ayrıntılar
| Birincil Dil | İngilizce |
|---|---|
| Konular | Sağlık Kurumları Yönetimi |
| Bölüm | Dahili Tıp Bilimleri Araştırma Yazıları |
| Yazarlar | |
| Yayımlanma Tarihi | 5 Haziran 2018 |
| Kabul Tarihi | 3 Mayıs 2018 |
| Yayımlandığı Sayı | Yıl 2018 |